RHF Fast Dry Castable
WHO WE ARE :
We not only provide the best service to World Top 500 Enterprises , also to YOU .
We can accept the Payment Term : LC 120 DAYS , D/P 90 DAYS, D/A-O/A 60 DAYS .
We have more 100 items Chinese National Patents .
Our Lab is Hennan province Refractory Engineering T&R Center
Our Tech Team include : PROFESSOR , DOCTORAL SUPERVISOR , SENIOR ENGINEER, EXPERT.
Our Project Team have rich experience for international Refractory Turn-Key Project .
We are not only to supply refractory products to YOU , We also want to share the KEY TECH with YOU.
High temp industrial furnace & fireplace / stove / boiler refractory products
- HONEYCOMB
- RHF Anchor Brick
- Platform／Sliding Rail ／Skimming／Launder Brick
- RHF Self Flow Castable
- Insulating Fiber Products
- Sic Kiln Furniture
- High Alumina Brick
- RHF Fast Dry Castable
- Outdoor/room Wood ovens/ stove / boiler/fireplace/burning furnace firebrick/brick
- Light Weight Castable
- RHF Burner Brick
- Clay Brick
- RHF High Alumina Castable
- Steel Fiber Castable
- Mullite Cordierite Kiln Furnitu
Fast Drying Castables and high performance refractory castables are similar. This kind of material is suitable for short installation, fast drying and furnace maintenance. Drying time is only 3 to 5 days, compared to the regular product, need 50% drying time, is an ideal material for furnace maintenance.
|
ITEM |
HIGH ALUMINA BASE |
MULLITE BASE |
|||||||
|
HD-LKJ55 |
HD-LKJ60 |
HD-LKJ65 |
HD-LKJ70 |
HD-MKJ60 |
HD-MKJ65 |
HD-MKJ70 |
HD-MKJ75 |
||
|
Al2O3 (%) ≥ |
55 |
60 |
65 |
70 |
60 |
65 |
70 |
75 |
|
|
BD (g/cm3) ≥ |
110℃ × 24h |
2.2 |
2.3 |
2.3 |
2.5 |
2.3 |
2.4 |
2.5 |
2.7 |
|
MOR(MPa) ≥ |
110℃ × 24 h |
6 |
7 |
8 |
8 |
7 |
8 |
9 |
10 |
|
1350℃ × 3 h |
8 |
10 |
10 |
11* |
10 |
10 |
12* |
12* |
|
|
CCS(MPa) ≥ |
110℃ × 24 h |
30 |
30 |
40 |
45 |
35 |
40 |
45 |
50 |
|
1350℃ × 3 h |
40 |
40 |
50 |
60* |
50 |
50 |
60* |
80* |
|
|
PLC (%) ≤ |
1350℃ × 3 h |
±0.5 |
±0.5 |
±0.5 |
±0.5* |
±0.5 |
±0.5 |
±0.5* |
±0.5* |
|
REF （℃） |
1400 |
1450 |
1500 |
1550 |
1500 |
1550 |
1600 |
1600 |
|