我公司从结构设计、组装技术、防结碳层处理、维护技术及涂层材料的开发等方面对焦炉炉门用内衬材料进行了全面的研究，采用优质的耐火合成材料，添加特殊的添加剂，研制出气孔率低、膨胀率低、热震稳定性强的大型焦炉预制件炉门砖。

Market fundamentals will be determined by the speed and size of the recovery from the global recession. At this stage, 2009 will be a tough year for global consumer demand, and deflationary conditions will remain until 2010.

镁橄榄石耐火材料的化学组成： (MgO)=37％～62％，m(MgO)／m(SiO2)波动于0.95～2.00。主晶相镁橄榄石 (M2S)=65％～75％。其余为MF和其他矿物。m (MgO)／m(SiO2) ＞1.33者往往含有少量方镁石。

Weakening global demand is providing some small advantage in that it is relieving supply tensions and removing shortages of skilled labour, goods and services within the industry. Combined with declines in energy costs, the industry is now faced with a reduction in production costs for the first time for many years.

磷酸盐结合砖高温体积稳定性低于普通烧成砖；磷酸盐结合的不烧砖的常温耐压强度高于普通烧成砖；磷酸盐结合砖的显气孔率较低。 磷酸盐结合不烧高铝砖的潮解问题。当热处理温度没有达到500℃时，结合剂生成AlH2P3O10，易吸湿转变成AlH2P3O10·2H2O，这正是磷酸铝试样经过300~400℃热处理后，露置在大气中发生溃散粉化。

We will attend Aluminum China 2014 at Shanghai on 9th., July-11th., July Location: Shanghai New International Expo Centre Booth No.: 3E57，Wecome you come to visit and guide to work. 

加水用耐火泥的特点是成本低，施工时使用方便，把耐火粉和结合剂一起搅拌直接加水15-20%左右的饮用水调制即可使用。磷酸结合的耐火泥有两种，一种是加入磷酸二氢铝，另外一种是用磷酸稀释后在使用时加入一定比例搅拌进行使用。