耐火材料用硅石行业标准
耐火材料用硅石行业标准（YB/T5268-2014）见表1，硅石产品粒度要求见表2。
|
表1耐火材料用硅石的理化指标(YB/T5268-2014) |
|||||
|
牌号 |
化学成分(质量分数)/% |
耐火度/℃ |
|||
|
SiO2 |
A12O3 |
Fe2O3 |
Cr2O3 |
||
|
GSN99A |
>99.0 |
60.25 |
<0.5 |
<0.15 |
1740 |
|
GSN99B |
>99.0 |
0.30 |
<0.5 |
0.15 |
1740 |
|
GSN98 |
>98.0 |
<0.50 |
<0.8 |
<0.20 |
1740 |
|
GSN97 |
>97.0 |
<1.00 |
<1.0 |
<0.30 |
1720 |
|
GSN96 |
>96.0 |
<1.30 |
<1.3 |
40.40 |
1700 |
|
注:1.表中“GSN”为“硅石耐”的拼音首字母大写。 2.产品中不应混入废石、角砾状硅石、风化石，不应混入外来杂质。 |
|||||
|
表2 硅石产品粒度要求 |
|||
|
粒度范围/mm |
最大粒度/mm |
允许波动范围/% |
|
|
下限 |
上限 |
||
|
20~40 |
50 |
10 |
8 |
|
40~60 |
70 |
10 |
8 |
|
60~120 |
140 |
10 |
5 |
|
120~160 |
170 |
10 |
8 |
|
160~250 |
260 |
8 |
6 |
Industry standard for silica for refractory materials
The silica industry standard for refractory materials (YB/T5268-2014) is shown in Table 1, and the particle size requirements for silica products are shown in Table 2.
|
Table 1 Physical and chemical indexes of silica for refractory materials (YB/T5268-2014) |
|||||
|
Brand |
Chemical composition (mass fraction)/% |
Refractoriness/℃ |
|||
|
SiO2 |
A12O3 |
Fe2O3 |
Cr2O3 |
||
|
GSN99A |
>99.0 |
60.25 |
<0.5 |
<0.15 |
1740 |
|
GSN99B |
>99.0 |
0.30 |
<0.5 |
0.15 |
1740 |
|
GSN98 |
>98.0 |
<0.50 |
<0.8 |
<0.20 |
1740 |
|
GSN97 |
>97.0 |
<1.00 |
<1.0 |
<0.30 |
1720 |
|
GSN96 |
>96.0 |
<1.30 |
<1.3 |
40.40 |
1700 |
|
Note :1. “GSN” in the table is the initials of “Silishi Nai”. 2. Waste rock, breccia silica, wind fossil should not be mixed into the product, and foreign impurities should not be mixed. |
|||||
|
Table 2 Particle size requirements of silica products |
|||
|
Size range/mm |
Maximum grain size/mm |
Allowable fluctuation range/% |
|
|
Floor |
Upper limit |
||
|
20~40 |
50 |
10 |
8 |
|
40~60 |
70 |
10 |
8 |
|
60~120 |
140 |
10 |
5 |
|
120~160 |
170 |
10 |
8 |
|
160~250 |
260 |
8 |
6 |